Fluorescent Comparison of Sr_2CeO_4 Prepared from Carbonate and Oxalate Precursor

【Author】

Shi Shikao~(1,2), Li Junmin(2,Wang Jiye, Wang Ruifen(2,Zhou Ji1. State Key Laboratory of New Ceramics and Fine Processing, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China; 2.College of Chemistry, Hebei Normal University, Shijiazhuang 050091, China)

【Abstract】

A blue-emitting phosphor powder, Sr_2CeO_4, was synthesized after heat-treatment to carbonate and oxalate precursors, which were obtained by co-precipitation reactions with respective ammonium compounds as precipitants. The phase formation and chemical purity of Sr_2CeO_4 powders were studied on XRD, TGA and XPS techniques. Their fluorescent performances were investigated and compared. The photoluminescence emission spectra for the phosphor prepared from respective precursors are similar, having a broad band with the peak at about 470 nm. However, their fluorescent intensities are different after heat-treatment at same conditions. The optimum condition to achieve superior Sr_2CeO_4 phosphor is confirmed.

【Keywords】

Sr_2CeO_4; phosphor; luminescence; co-precipitation;rare earths

References

To explore the background and basis of the node document

Springer Journals Database

Total: 6 articles

  • [1] PietersonP ,;SovernaS ;MeijerinkA, OnthenatureoftheluminescenceofSr2CeO4, J .Electrochem.Soc,
  • [2] DanielsonE ,;DevenneyM ;GiaquintaDM ,etal, Arare earthphosphorcontainingone dimensionalchainsidenti fiedthroughcombinatorialmethods, Science, Science (Science)
  • [3] MasuiT ,;ChigaT ;ImanakaN ,etal, Synthesisandlumi nescenceofSr2CeO4fineparticles, Mater.Res.Bull, Materials Research Bulletin (Materials Research Bulletin)
  • [4] DanielsonE ,;DevenneyM ;GiaquintaDM ,etal, X raypowderstructureofSr2CeO4:anewluminescentmaterialdiscoveredbycombinatorialchemistry, J .Mol.Struct,

More>>

Similar documents

Documents that have the similar content to the node document

More>>